Specifications of impregnated carbon graphite mainly include indicators such as density, resistivity, flexural strength, compressive strength, thermal expansion coefficient, ash content and particle size. The following are detailed information on several common specifications:
TC170: density is 1.70 g/cm³, resistivity is 8.0 μωm, flexural strength is 21.0 MPa, compressive strength is 42.0 MPa, thermal expansion coefficient is 2.9×10⁻⁶/℃, ash content is 0.3%, and particle size is 4.0 mm.
TZ160: density is 1.60 g/cm³, resistivity is 8.0 μωm, flexural strength is 18.0 MPa, compressive strength is 36.0 MPa, thermal expansion coefficient is 2.9×10⁻⁶/℃, ash content is 0.3%, and particle size is 2.0 mm.
TZ170: density is 1.70 g/cm³, resistivity is 8.0 μωm, flexural strength is 20.0 MPa, compressive strength is 40.0 MPa, thermal expansion coefficient is 2.9×10⁻⁶/℃, ash content is 0.3%, and particle size is 2.0 mm.
TX170: density is 1.70 g/cm³, resistivity is 7.8 μωm, flexural strength is 20.0 MPa, compressive strength is 40.0 MPa, thermal expansion coefficient is 2.9×10⁻⁶/℃, ash content is 0.3%, and particle size is 0.8 mm.
TX172: density 1.72 g/cm³, resistivity 7.5 μωm, flexural strength 22.0 MPa, compressive strength 44.0 MPa, thermal expansion coefficient 2.9×10⁻⁶/℃, ash content 0.3%, particle size 0.8 mm.
TX174: density 1.74 g/cm³, resistivity 7.5 μωm, flexural strength 24.0 MPa, compressive strength 48.0 MPa, thermal expansion coefficient 2.9×10⁻⁶/℃, ash content 0.3%, particle size 0.8 mm.
TX185: density 1.85 g/cm³, resistivity 7.0 μωm, flexural strength 36.0 MPa.
These specifications indicate that impregnated carbon graphite has high density, good conductivity and mechanical strength, suitable for various industrial applications.