Description

Send Inquiry

Antimony impregnated graphite rods are wear-resistant, corrosion-resistant, high-temperature-resistant and lubricating. They can be used to manufacture mechanical seals, bushings, bearings, seals and other accessories. Antimony impregnated graphite rods have a higher working temperature than resin impregnated graphite rods, and the working temperature can reach 480 degrees Celsius.

Our company specializes in the production of impregnated resin (M106K, M120K), impregnated antimony (M106D, M120D), impregnated copper, impregnated babbitt alloy, impregnated silver graphite rods, quality assurance, rest assured to purchase. If you have any needs, please contact us.

Impregnated carbon rods

For making mechanical seals and graphite bearings

used in food, beverage, textile, chemical and other industries of the conveyor, drying machine, textile machines, submersible pump motor bearing, these parts such as grease lubricant Inevitably cause pollution, and graphite bearing strong self lubrication, corrosion resistance, don't use into lubricating oil Line running for a long time.

application 500

Impregnated graphite datasheet

Type	impregnated material	bulk density (g/cm³)	Hardness shore (HS)	Flexural Strength (MPA)	compressive strength(MPA)	Porosity ( %)	Coeficient of expansion (10^-6/^oC)	Max working temperature (^oC)
M106 G	Silver(G)	2.80	80	65	190	2.0		900
M106P	copper(P)	2.20	80	70	210	3.0	6.8	400
M106D	Antimony(D)	2.2-2.3	85	62	190	2.2	7.0	480
M154D	Antimony(D)	2.2-2.3	70	55	150	2.2	7.0	480
M106A	aluminium alloy(A)	2.00	40	60	120	2.5	7.3	350
M106B	Babbitt Alloy	2.50	80	40	70	7.0	5.2	220
M106K	resin	1.75	80	60	176	1.0	4.0	200
M154K	resin	1.70	70	50	100	1.5	3.5	200